The elimination of the additional defect healing post‐treatment step in asymmetric hollow fiber manufacturing would result in a significant reduction in membrane production cost. However, obtaining integrally skinned polymeric asymmetric hollow fiber membranes with an ultrathin and defect‐free selective layer is quite challenging. In this study, P84® asymmetric hollow fiber membranes with a highly thin (~56 nm) defect‐free skin were successfully fabricated by fine tuning the dope composition and spinning parameters using volatile additive (tetrahydrofuran, THF) as key parameters. An extensive experimental and theoretical study of the influence of volatile THF addition on the solubility parameter of the N‐methylpyrrolidone/THF solvent mixture was performed. Although THF itself is not a solvent for P84®, in a mixture with a good solvent for the polymer, like N‐Methyl‐2‐pyrrolidone (NMP), it can be dissolved at high THF concentrations (NMP/THF ratio > 0.52). The as‐spun fibers had a reproducible ideal CO2/N2 selectivity of 40, and a CO2 permeance of 23 GPU at 35 °C. The fiber production can be scaled‐up with retention of the selectivity.@en

Carbon capture and storage (CCS) using membranes for the separation of CO2 holds great promise for the reduction of atmospheric CO2 emissions from fuel combustion and industrial processes. Among the different process outlines, post-combustion CO2 capture could be easily implemented in existing power plants. However, for this technology to become viable, new membrane materials have to be developed. In this article we present the development of high performance mixed matrix membranes (MMMs) composed of ZIF-94 filler and 6FDA-DAM polymer matrix. The CO2/N2 separation performance was evaluated by mixed gas tests (15CO2:85N2) at 25 °C and 1–4 bar transmembrane pressure difference. The CO2 membrane permeability was increased by the addition of the ZIF-94 particles, maintaining a constant CO2/N2 selectivity of ~22. The largest increase in CO2 permeability of ~ 200% was observed for 40 wt% ZIF-94 loading, reaching the highest permeability (2310 Barrer) at similar selectivity among 6FDA-DAM MMMs reported in literature. For the first time, the ZIF-94 metal organic framework crystals with particle size smaller than 500 nm were synthesized using nonhazardous solvent (tetrahydrofuran and methanol) instead of dimethylformamide (DMF) in a scalable process. Membranes were characterized by three non-invasive image techniques, i.e. SEM, AFM and nanoscale infrared imaging by scattering-type scanning near-field optical microscopy (s-SNOM). The combination of these techniques demonstrates a very good dispersion and interaction of the filler in the polymer layer, even at very high loadings.@en