This study investigates the microbiologically influenced corrosion (MIC) of X80 steel accelerated by the phototrophic bacterium Rhodopseudomonas palustris TIE-1. The photorespiration plays a key role in promoting extracellular electron transfer (EET)-induced MIC. In the early corrosion stage, unstable localized corrosion dominated in the dark, while intense diffusion-controlled corrosion occurs in light. Compared to the sterile anaerobic medium, R. palustris TIE-1 accelerated corrosion of X80 steel, with a significantly higher corrosion rate under light conditions, approximately three times that of dark conditions. Inhibition of photosynthetic electron transfer or cessation of photostimulation resulted in pronounced reduction in the corrosion rate.

Herein, we report the development of a self-sensing and active corrosion protection coating which incorporates pH-sensitive multilayer chitosan/alginate-covered CaCO₃ microcontainers containing 1,10-phenanthrolin-5-amine (APhen). The microcontainers can respond to pH variation to release APhen which serves not only as a corrosion indicator but also as an inhibitor. An epoxy coating doped with 5 wt% microcontainers exhibited improved corrosion performance and was capable of inhibiting corrosion spreading from the damaged area in a 3.5 wt% NaCl solution. The salt spray test showed that corrosion damage can be quickly detected by the appearance of a red color within 2 min.