In-Depth Analysis of the Conversion Mechanism of TiSnSb vs Li by Operando Triple-Edge X-ray Absorption Spectroscopy
A Chemometric Approach
Marcus Fehse (Universite de Picardie Jules Verne, TU Delft - Applied Sciences, European Synchrotron Radiation Facility)
Ali Darwiche (Université de Montpellier)
Moulay T. Sougrati (CNRS FR3459, Université de Montpellier)
Erik M. Kelder (Universite de Picardie Jules Verne, TU Delft - Applied Sciences)
Alan V. Chadwick (Universite de Picardie Jules Verne, University of Kent)
Maria Alfredsson (University of Kent, Universite de Picardie Jules Verne)
Laure Monconduit (CNRS FR3459, Université de Montpellier, Universite de Picardie Jules Verne)
Lorenzo Stievano (CNRS FR3459, Universite de Picardie Jules Verne, Université de Montpellier)
More Info
expand_more
Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.
Abstract
The electrochemical cycling mechanism of the ternary intermetallic TiSnSb, a promising conversion-type negative electrode material for lithium batteries, was thoroughly studied by operando X-ray absorption spectroscopy (XAS) at three different absorption edges, i.e., Ti, Sn, and Sb K-edge. Chemometric tools such as principal component analysis and multivariate curve resolution-alternating least squares were applied on the extensive data set to extract the maximum contained information in the whole set of operando data. The evolution of the near-edge (XANES) fingerprint and of the extended fine-structure (EXAFS) of the XAS spectra confirms the reversibility of the conversion mechanism, revealing that Ti forms metallic nanoparticles upon lithiation and binds back to both Sn and Sb upon the following delithiation. The formation of both Li7Sn2 and Li3Sb upon lithiation was also clearly confirmed. The application of chemometric tools allowed the identification of a time shift between the reaction processes of Sn and Sb lithiation, indicating that the two metals do not react at the same time, in spite of a certain overlap between their respective reaction. Furthermore, XANES and EXAFS fingerprint show that the Ti-Sn-Sb species formed after one complete lithiation/delithiation cycle is distinct from the starting material TiSnSb.