From single- to double-first-order magnetic phase transition in magnetocaloric Mn1−xCrxCoGe compounds
N.T. Trung
V. Biharie
L. Zhang
L. Caron
K.H.J. Buschow
E.H. Brück
More Info
expand_more
Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.
Abstract
Substitution of some Cr for Mn atoms in MnCoGe was employed to control the magnetic and structural transitions in this alloy to coincide, leading to a single first-order magnetostructural transition from the ferromagnetic to the paramagnetic state with a giant magnetocaloric effect observed near room temperature. Further increase in the Cr content in the Mn1?xCrxCoGe alloys can induce another first-order magnetoelastic transition from the antiferromagnetic to the ferromagnetic state occurring at lower temperature. The giant magnetocaloric effect as well as the simultaneous tunability of the two magnetic transitions make these materials promising for future cooling applications.