Electrochemical behavior of zirconium in molten LiF-KF-ZrF<sub>4</sub> at 600 °C

Journal article (2016)

Authors

L. Xu Northeastern University China, OLD Metals Processing, Microstructures and Properties
Y. Xiao (OLD) MSE-3 , Anhui University of Technology
Qian Xu Shanghai University
Anthonie Van Sandwijk Zr-Hf-Ti Metallurgie B.V.
J. Li OLD Metals Processing, Microstructures and Properties , Liaoning University
Z. Zhao Anhui University of Technology
Qiushi Song Northeastern University China
Y. Yang Anhui University of Technology, (OLD) MSE-3
Research Group
(OLD) MSE-3
More Info
expand_more

Published Date

2016

Language

English

Reuse Rights

Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.

Research Group

(OLD) MSE-3

Abstract

In this paper, a detailed study of the electrochemical behavior of zirconium in the molten LiF-KF-ZrF4 system on an inert molybdenum electrode was carried out at 600 °C. Several electrochemical techniques were employed such as cyclic voltammetry, chronoamperometry and square wave voltammetry. The reduction of zirconium was found to be a multi-step process that at the potentials of 1.15, 1.50 and 1.62 V versus Pt, the corresponding cathodic reactions of Zr4+/Zr2+, Zr2+/Zr+ and Zr+/Zr occurred. The result was further confirmed by the theoretical calculation of the number of transferred electrons according to the cyclic voltammetry and square wave voltammetry analysis. Moreover, based on the cyclic voltammograms, the diffusion coefficient of Zr4+ ions in the eutectic LiF-KF containing 1 wt% ZrF4 at 600 °C was estimated to be about 8.31 × 10-6 cm2 s-1. The present electrochemical study on zirconium in the molten fluoride system will be a theoretical reference for future zirconium electrorefining from Zr alloy or scraps.