An experimental and numerical investigation of secondary char formation in hydrothermal carbonization

revealing morphological changes via hydrodynamics

Journal Article (2025)
Author(s)

Omar M. Abdeldayem (TU Delft - Sanitary Engineering, IHE Delft Institute for Water Education)

Capucine Dupont (IHE Delft Institute for Water Education)

David Ferràs (IHE Delft Institute for Water Education)

Maria Kennedy (IHE Delft Institute for Water Education, TU Delft - Sanitary Engineering)

Research Group
Sanitary Engineering
DOI related publication
https://doi.org/10.1039/d4ra08995b
More Info
expand_more
Publication Year
2025
Language
English
Research Group
Sanitary Engineering
Issue number
16
Volume number
15
Pages (from-to)
12723-12738
Reuse Rights

Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.

Abstract

Hydrothermal carbonization (HTC) research has mainly focused on primary char production, with limited attention to secondary char, which is formed through polymerization and condensation of dissolved organic compounds in the liquid phase. This research aims to address this gap via an experimental investigation of the impact of stirring on the mass and carbon balance of HTC reaction products, surface functional groups, and surface morphology of secondary char, using fructose as a model compound. A 3D hydrodynamic simulation model was developed for a two-liter HTC stirred reactor. The experimental results indicated that stirring did not significantly influence the pH, mass, carbon balance, and surface functional groups of secondary char produced under the range of experimental conditions (180 °C, 10% biomass to water (B/W) ratio, and a residence time of 0-120 min) studied. Nonetheless, it was observed that a stirring rate of 200 rpm influenced the morphology and shape of the secondary char microspheres, leading to a significant increase in their size i.e., from 1-2 μm in unstirred conditions compared with 70 μm at a stirring rate of 200 rpm. This increase in size was attributed to the aggregation of microspheres into irregular aggregates at stirring rates > 65 rpm and residence times > 1 h. The hydrodynamic model revealed that high turbulence of Re > 104 and velocities > 0.17 m s−1 correlated with regions of secondary char formation, emphasizing their role in particle aggregation. Particle aggregation is significant above a stirring rate of 65 rpm, which corresponds to the onset of turbulent flow in the reactor. Finally, a mechanism is proposed, based on reactor hydrodynamics under stirred conditions, that explains secondary char deposition on the reactor walls and stirrer.