Investigating the flexural strength of recycled cast glass

Journal Article (2020)
Author(s)

T. Bristogianni (TU Delft - Applied Mechanics)

Faidra Oikonomopoulou (TU Delft - Structural Design & Mechanics)

R. Yu (TU Delft - Applied Mechanics)

F. Veer (TU Delft - Structural Design & Mechanics)

R. Nijsse (TU Delft - Applied Mechanics)

Research Group
Applied Mechanics
Copyright
© 2020 T. Bristogianni, F. Oikonomopoulou, R. Yu, F.A. Veer, R. Nijsse
DOI related publication
https://doi.org/10.1007/s40940-020-00138-2
More Info
expand_more
Publication Year
2020
Language
English
Copyright
© 2020 T. Bristogianni, F. Oikonomopoulou, R. Yu, F.A. Veer, R. Nijsse
Related content
Research Group
Applied Mechanics
Issue number
3
Volume number
5
Pages (from-to)
445–487
Reuse Rights

Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.

Abstract

Currently, tons of high quality commercial glass are down-cycled or landfilled due to contaminants that prevent close-loop recycling. Yet, this glass is potentially a valuable resource for casting robust and aesthetically unique building components. Exploring the potential of this idea, different types of non-recyclable silicate glasses are kiln-cast into 30 × 30 × 240 mm beams, at relatively low temperatures (820–1120∘C). The defects occurring in the glass specimens due to cullet contamination and the high viscosity of the glass melt, are documented and correlated to the casting parameters. Then, the kiln-cast specimens and industrially manufactured reference beams are tested in four-point bending, obtaining a flexural strength range of 9–72 MPa. The results are analysed according to the role of the chemical composition, level of contamination and followed casting parameters, in determining the flexural strength, the Young’s modulus and the prevailing strength-limiting flaw. Chemical compositions of favourable performance are highlighted, so as critical flaws responsible for a dramatic decrease in strength, up to 75%. The defects situated in the glass bulk, however, are tolerated by the glass network and have minor impact on flexural strength and Young’s modulus. The prerequisites for good quality recycled cast glass building components are identified and an outline for future research is provided.