Annealing Effects on Cu Migration in the Colloidal Synthesis of Pd-Chalcogenides Nanoheterostructures
Suvodeep Sen (University of Limerick)
Niraj Nitish Patil (University of Limerick)
Ankita Bora (University of Limerick)
Manoj Palabathuni (University of Limerick)
Temilade Esther Adegoke (University of Limerick)
Kevin M. Ryan (University of Limerick)
Kevin Rossi (TU Delft - Team Kevin Rossi)
Shalini Singh (University of Limerick)
More Info
expand_more
Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.
Abstract
Heterostructuring nanocrystals into a modular metal-semiconductor configuration enables tunable and novel functionalities. Such combinations at the nanoscale equip hybrid structures with unique electronic, optical, and catalytic properties unobserved in single-phase materials. Here, we report the hot-injection synthesis of Pd-Cu3Pd13S6.65Te0.35 nanoheterostructures (NHCs) from PdCu nanoalloy seeds. First, the growth of Pd-rich chalcogenide nanocrystals was initiated over the preformed PdCu surface through simultaneous sulfidation and tellurization, followed by their transformation into Pd-Cu3Pd13S6.65Te0.35 NHCs. By strategically employing moderate-temperature annealing, we achieved the complete migration of Cu+ due to the higher reactivity of Cu in comparison to Pd at that temperature, establishing a novel mechanistic relationship between cation mobility and temperature. This strategy enables controlled semiconductor domain formation and targeted metal migration. The NHCs showed efficient and stable electrocatalytic hydrogen evolution with low Tafel values in acidic media, outperforming conventional nanoelectrocatalysts. Computational analysis identified the active sites responsible for the observed catalytic performance.