Blending additional calcium hydroxide into LC³ with high amount of calcined clay to modify fresh and hardened properties

Abstract

Adding hydrated lime (CH) into blended cement incorporating high volume of Supplementary Cementitious Materials (SCMs) is a viable method to provide the necessary calcium hydroxide for the pozzolanic reaction, thereby improving the mechanical performance at later stages. However, the effects of relatively small dosages of CH on the rheological properties and resulting microstructure of limestone-calcined clay cement (LC3) remain unclear. This paper aims to investigate the influence of a small CH addition on the fresh and hardened properties of LC3 systems, in which Portland cement is largely replaced (80 wt%) by limestone and calcined clay. The results indicate that the additional CH notably reduces the water film thickness, leading to increased dynamic yield stress, plastic viscosity and re-flocculation. A delay in the elasticity development and static yield stress evolution within the first 1.5 h was observed with the addition of 2.5 wt% CH, attributed to the initial dissolution of CH, which is mitigated by using 10 wt% CH. Furthermore, additional CH accelerated early-age hydration and facilitated long-term pozzolanic reactions, resulting in the increased amount of C-(A)-S-H gel and AFm phases, and reduced porosities after 7 and 28 days. These chemical effects could well compensate the high air void content caused by the high viscosity, and therefore contributes to mortars with higher compressive strengths than plain LC3 at later ages.