Synthesis, Characterization and Properties of Semi-aromatic Polyamide Thermosets
M. LI (TU Delft - Novel Aerospace Materials)
More Info
expand_more
Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.
Abstract
The work presented in this thesis describes a route towards semi-crystalline polyamide (PA 10T) thermosets. A mild temperature solution polymerization method was developed to synthesize melt-processable PA 10T precursors with crosslinkable functionalities. These functionalities can be placed at the polymer chain-ends or as pedent groups on the polymer backbone. The reactive precursors were thermally cured into polyamide thermosets and their morphology and thermo-mechanical properties of the final thermosets. Finally, semi-crystalline PA 10T thermoset films were evaluated as single-component high-temperature shape memory materials.