Substantial enhancement of corrosion resistance and bioactivity of magnesium by incorporating calcium silicate particles

Journal article (2016)

Authors

Z. Huan Chinese Academy of Sciences
Chen Xu Chinese Academy of Sciences
Bing Ma Chinese Academy of Sciences
J. Zhou Biomaterials & Tissue Biomechanics - Mechanical, Maritime and Materials Engineering
J. Chang Chinese Academy of Sciences
Research Group
Biomaterials & Tissue Biomechanics (Mechanical, Maritime and Materials Engineering) (TU Delft)
More Info
expand_more

Published Date

2016

Language

English

Reuse Rights

Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.

Faculty

Mechanical, Maritime and Materials Engineering

Department

Biomechanical Engineering

Research Group

Biomaterials & Tissue Biomechanics

Abstract

Biodegradable metal matrix composites (MMCs) with pure magnesium as the matrix and bioceramic calcium silicate (CS) as the reinforcement phase were fabricated by means of spark plasma sintering (SPS). The microstructure, mechanical properties and degradation behavior of the composites as well as the cellular responses to these composites were investigated. The formation of CS networks in the Mg matrix was observed when the CS content reached 20%. Among the composites with CS weight percentages ranging from 10% to 40%, the composite containing 20% CS possessed the highest structural compactness and compressive strength. Immersion tests in simulated body fluid (SBF) revealed that the Mg-20% CS composite exhibited a substantially enhanced corrosion resistance as compared with pure Mg, which was attributed to the formation of a hydroxyapatite (HA) layer on the surface as a result of the presence of the CS networks throughout the Mg matrix. In addition, ionic products from the interaction between the Mg-20% CS composite and SBF brought about a significant stimulatory effect on the alkaline phosphate (ALP) expression of MC3T3-E1 osteoblast cells. Our results indicate that CS is an effective reinforcement phase to improve both the corrosion resistance and bioactivity of Mg and the Mg-CS composites developed in this research are able to overcome the inherent drawbacks of magnesium as a biodegradable implant material.