High performance quasi-isotropic thin-ply carbon/glass hybrid composites with pseudo-ductile behaviour loaded off-axis
Mohamad Fotouhi (University of the West of England)
M. Jalalvand (University of Strathclyde)
M. Saeedifar (TU Delft - Structural Integrity & Composites)
Bill Xiao (University of Bristol)
Michael R Wisnom (University of Bristol)
More Info
expand_more
Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.
Abstract
The aim of this work was to investigate the effect of loading angle variation on the pseudo-ductility of quasi-isotropic (QI) hybrid composite laminates. Previously, hybrids of thin-ply carbon fibres and standard glass fibres were found to have an excellent pseudo-ductile behaviour both in unidirectional (UD) and QI configurations when subjected to axial tension in the fibres’ orientations. In this work, the QI laminates, with 60° intervals, have been subjected to a quasi-static tensile load at various off-axis orientations – i.e. 5°, 10° and 20°. The QI hybrid composites were made by sandwiching a QI T300-carbon laminate between the two halves of a QI S-glass laminate. The results showed a pseudo-ductile behaviour with a linear elastic part and a desirable plateau for all the loading directions, however the pseudo-ductile strain decreases when increasing the off-axis angle. Comparing the 20° off-axis with the other cases, there was more active matrix cracking damage before fragmentation in the 20° off-axis plies and it failed earlier than the other samples. Acoustic emission (AE) results confirmed this, with more matrix cracking related AE signals in the 20° off-axis case compared to the other configurations.