Uncovering the white etching area and crack formation mechanism in bearing steel
Ksenija Nikolic (Strategisch Initiatief Materialen, Universiteit Gent)
V. Mattos Ferreira (TU Delft - Team Maria Santofimia Navarro)
Loïc Malet (Ecole Polytechnique de Bruxelles)
T. Depover (Universiteit Gent)
Kim Verbeken (Universiteit Gent)
R. Petrov (TU Delft - Team Maria Santofimia Navarro, Universiteit Gent)
More Info
expand_more
Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.
Abstract
The microstructure of a damaged bearing from the field was characterized in this work with the intention to better understand microstructural features behind formation of White Etching Cracks (WEC) in bearings. Microstructural characterization of the altered white etching area (WEA) involved conventional electron backscattered diffraction (EBSD), followed by transmission electron microscopy (TEM), and transmission Kikuchi diffraction (TKD). In addition, automated crystallographic orientation mapping in TEM was performed on lamellae from selected regions of the WEA extracted via focus ion beam milling. The results revealed that the orientation of detectable grains within WEA is similar to that of the vicinal bulk material. WEA consists of small spherical grains (average 30 nm) and the orientation of the grains varied significantly in the deformed zone, suggesting that recrystallization had occurred. The interface between bulk material and the deformed zone is very sharp. Furthermore, needle-like grains, most likely originating from the zone undergoing only modest levels of severe plastic deformation, occurred in WEA. The occurrence of different grain sizes in WEA and incomplete plastic deformation strongly support the hypothesis of WEC formation via severe plastic deformation followed by recrystallization.