Effect of Grain Refinement on Structure Evolution, “Floating” Grains, and Centerline Macrosegregation in Direct-Chill Cast AA2024 Alloy Billets

Journal article (2007)
Department
Materials Science and Engineering (Mechanical, Maritime and Materials Engineering) (TU Delft)
Copyright: © 2007 The Authors; The Minerals, Metals & Materials Society and ASM International; Springer
More Info
expand_more

Published Date

13-12-2007

Reuse Rights

Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.

Source:

Metallurgical and Materials Transactions A

ISSN:

1543-1940

Faculty

Mechanical, Maritime and Materials Engineering

Department

Materials Science and Engineering

Abstract

Direct-chill (DC) cast billets 192 mm in diameter of an Al-Cu-Mg alloy were examined in detail with the aim to reveal the effects of grain refining (GR) and casting speed on structure, “floating” grains, and centerline macrosegregation. Experimental results show that grain size and dendrite arm spacing (DAS) tend to coarsen toward the billet center with a local refinement DAS in the center. In GR billets, grain size does not change much with the cooling rate, casting speed, and grain refiner amount. Coarse-DAS (floating) grains are observed around the billet axis regardless of GR and the amount of Ti, though their amount is significantly higher in GR billets. Macrosegregation profiles show a negligible influence of GR, while the effect of casting speed is large. The concept of solute-depleted floating grains contributing to the centerline macrosegregation is substantiated by microsegregation measurements, which show that, independent of GR, coarse dendrite branches have a depleted concentration plateau in contrast to the fine dendrite arms.