Mo(AlxSi1−x)2 healing particles for high temperature ceramics and encapsulation by selective oxidation of aluminium

Journal Article (2023)
Author(s)

Z. Ding (TU Delft - Team Marcel Hermans)

J.C. Brouwer (TU Delft - Team Marcel Hermans)

C. Kwakernaak (TU Delft - Team Maria Santofimia Navarro)

Jia-Ning Zhu (TU Delft - Team Vera Popovich)

V. Popovich (TU Delft - Team Vera Popovich)

M.J.M. Hermans (TU Delft - Team Marcel Hermans)

W.G. Sloof (TU Delft - Team Joris Dik)

Research Group
Team Marcel Hermans
Copyright
© 2023 Z. Ding, J.C. Brouwer, C. Kwakernaak, Jia-Ning Zhu, V. Popovich, M.J.M. Hermans, W.G. Sloof
DOI related publication
https://doi.org/10.1016/j.matdes.2022.111577
More Info
expand_more
Publication Year
2023
Language
English
Copyright
© 2023 Z. Ding, J.C. Brouwer, C. Kwakernaak, Jia-Ning Zhu, V. Popovich, M.J.M. Hermans, W.G. Sloof
Research Group
Team Marcel Hermans
Volume number
225
Reuse Rights

Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.

Abstract

To prevent premature triggering of the healing reaction in Mo-Si containing self-healing thermal barrier coating system, an oxygen impenetrable shell (α-Al2O3) around the sacrificial healing particles (MoSi2) is desired. Here an encapsulation method is presented through selective oxidation of Al in Mo(AlxSi1-x)2 particles. Healing particles of Mo(AlxSi1-x)2 is designed in terms of alumina shell thickness, particle size and fraction Al dissolved. By replacing Si by Al in MoSi2 up to the maximum solubility (x = 0.65) a strong crack healing ability is maintained (relative volume expansion ≥ 40 %). The formed exclusive α-Al2O3, featuring a two-layered structure, results from a counter-diffusion process along the grain boundaries, and its oxidation kinetics fits well with the 3D diffusion-Jander model. After 16 h exposure in gaseous ambient with a pO2 of 5 × 10-10 atm. at 1100 °C, a closed and dense shell of α-Al2O3 is formed with a thickness of about 1.3 µm. The oxide shell produced under this condition provided healing particles with significantly improved stability upon exposure to high pO2 of 0.2 atm. at 1100 °C for 50 h. The particles after exposure feature an inner core of MoSi2 with Al completely consumed and an oxide shell of α-Al2O3.