Microstructural phenomena in pearlitic railway steels
V. Ferreira (TU Delft - Team Maria Santofimia Navarro)
J. Sietsma – Promotor (TU Delft - Team Joris Dik)
Roumen Petrov – Promotor (Universiteit Gent, TU Delft - Team Maria Santofimia Navarro)
More Info
expand_more
Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.
Abstract
The railway industry constantly seeks advancements in train speed, axle load capacity, reliability, and rail longevity. Rails undergo complex and severe loading during operation due to wheel/rail contact, resulting in two main damage mechanisms: rolling contact fatigue (RCF) andwear. Furthermore, frictional heating during wheel/rail contact causes local temperature rise, leading to microstructural processes on the rail surface, known as white etching layer (WEL) and brown etching layer (BEL). This project aims to gain insight into the microstructural changes in rail steels, with a primary focus on understanding the origins of detrimental surface layers like WEL and BEL. By achieving this understanding, the lifespan of the rails can be extended and the maintenance frequency can be reduced, which has significant effects on the sustainability of the railway network as well as overall life cycle costs. Additionally, the project explores the microstructural characteristics of recently developed steel grades with enhanced resistance to rolling contact fatigue....