High strain rate torsional response of maraging steel parts produced by laser powder bed fusion techniques
Deformation behavior and constitutive model
S. Dehgahi (University of New Brunswick)
H. Pirgazi (Universiteit Gent)
M. Sanjari (Natural Resources Canada, University of New Brunswick)
P. Seraj (University of New Brunswick)
A. Odeshi (University of Saskatchewan)
L.A.I. A.I. Kestens (TU Delft - Team Kevin Rossi)
M. Mohammadi (University of New Brunswick)
More Info
expand_more
Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.
Abstract
The deformation performance of maraging steel samples fabricated using the laser powder bed fusion technique was evaluated using the split Hopkinson torsion bar (SHTB) test. Thin-walled tubular maraging steel samples were deformed under dynamic torsional loading at strain rates of 260 s−1 to 720 s−1 using twist angles varying from 3 to 12°. Microstructural and textural investigations were carried out on deformed samples using the electron backscatter diffraction technique and scanning electron microscopy. Results showed that maraging steel samples fractured when deformed using an angle of twist of 12° and strain rate of 650 s−1. As a result of deformation localization at high strain rates, adiabatic shear bands are developed in some thin-walled tubular torsion specimens deformed using the 12-degree angle of twist, leading to fracture. Textural studies showed that texture weakening occurred with an increment in strain rate ascribable to grain fragmentation. In this study, two models (empirically and semi-empirically) were employed for describing maraging steel performance during high strain-rate torsional loading. Simulation results based on Kobayashi-Odd and Nemat-Nasser models agreed well with the experimental data.