Loading rate dependency of strain energy release rate in mode I delamination of composite laminates

Journal article (2021)

Authors

Amin Ekhtiyari Iran University of Science and Technology
R.C. Alderliesten Structural Integrity & Composites - Aerospace Engineering
Mahmood M. Shokrieh Iran University of Science and Technology
Research Group
Structural Integrity & Composites (Aerospace Engineering) (TU Delft)
Copyright: © 2021 Amin Ekhtiyari, R.C. Alderliesten, Mahmood M. Shokrieh
DOI: https://doi.org/10.1016/j.tafmec.2021.102894
More Info
expand_more

Published Date

2021

Language

English

Reuse Rights

Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.

Faculty

Aerospace Engineering

Department

Aerospace Structures & Materials

Research Group

Structural Integrity & Composites

Abstract

This work aims at studying the loading rate dependency of mode I delamination growth in CFRPs, using typical fracture toughness analysis through both the R-curve and the crack tip opening rate. The average SERR is a method of data reduction based on energy balance which has been previously introduced to characterize delamination growth under different types of loading conditions in a similar manner. In the present research, the application of this method was extended to further analyze the results of delamination experiments at different loading rates. Mode I delamination tests on double cantilever beam specimens were performed at displacement rates varying from standard quasi-static testing up to 400 mm/s. A clear decrease in the propagation fracture toughness as well as in the average SERR was observed at high loading rates. The reduced fracture resistance at elevated rates was physically explained in correlation with fiber bridging, fiber breakage, and matrix cleavage observed in fracture surfaces via scanning electron microscopy.