Print Email Facebook Twitter Optimization of intrinsic self-healing silicone coatings by benzotriazole loaded mesoporous silica Title Optimization of intrinsic self-healing silicone coatings by benzotriazole loaded mesoporous silica Author Chen, Guangmeng (Northwestern Polytechnical University) Wen, Shifeng (Northwestern Polytechnical University) Ma, Jiacheng (Northwestern Polytechnical University) Sun, Zhiyong (Luoyang Ship Material Research Institute) Lin, Cunguo (Luoyang Ship Material Research Institute) Yue, Zhufeng (Northwestern Polytechnical University) Mol, J.M.C. (TU Delft Team Arjan Mol) Liu, M. (TU Delft Energy Technology; Xi’an Jiaotong University) Date 2021 Abstract Multifunctional intrinsic self-healing polymers (ISP) are gaining increasing attention these days, and many studies have been devoted to solving the conflict between achieving high mechanical polymer strength and active polymer chain diffusion. In this research, we developed an optimized self-healing composite coating by adding Benzotriazole (BTA) loaded nano silica (SiO2@BTA) to a dynamic cross-linked Polydimethylsiloxane (PDMS) network，which allows substantial and fast healing of the material integrity upon damage due to the hydrogen interaction between urea and BTA. BTA leaching tests demonstrated a longer release profile during the coating service life and corrosion tests in a 3.5 wt% NaCl aqueous solution indicated that the SiO2@BTA modified PDMS coating shows enhanced corrosion protection of carbon steel upon coating damage. Moreover, after addition of SiO2@BTA, the material failure strength increased from ~1.5 MPa to ~5.5 MPa, and the healing efficiency increased from ~59% to ~90% for 24 h healing at room temperature. Above all, this research provides an intrinsic self-healing coating design method to improve the mechanical strength and the self-healing ability of the ISP as well as enhancing the coating's corrosion protection ability. Subject BTA leachingCorrosion protectionMechanical strengthSelf-healing coatingUrea hydrogen To reference this document use: http://resolver.tudelft.nl/uuid:cabd41d2-550f-407a-b2d9-ccf54e368293 DOI https://doi.org/10.1016/j.surfcoat.2021.127388 Embargo date 2021-12-07 ISSN 0257-8972 Source Surface and Coatings Technology, 421 Bibliographical note Green Open Access added to TU Delft Institutional Repository 'You share, we take care!' - Taverne project https://www.openaccess.nl/en/you-share-we-take-care Otherwise as indicated in the copyright section: the publisher is the copyright holder of this work and the author uses the Dutch legislation to make this work public. Part of collection Institutional Repository Document type journal article Rights © 2021 Guangmeng Chen, Shifeng Wen, Jiacheng Ma, Zhiyong Sun, Cunguo Lin, Zhufeng Yue, J.M.C. Mol, M. Liu Files PDF 1_s2.0_S0257897221005624_main.pdf 4.46 MB Close viewer /islandora/object/uuid:cabd41d2-550f-407a-b2d9-ccf54e368293/datastream/OBJ/view