The influence of different types of anodic layers on the fatigue properties of 202U-T3 and 7056-T6 sheet material

Constant amplitude and flight simulation fatigue tests have been carried out on sulphuric acid, chromic acid and phosphoric acid anodized specimens. A comparison was made with the fatigue behaviour of bare sheet material. Before fatigue testing the fracture strain of the anodic layers was determined.

Influence of corrosion damage on fatigue crack initiation

The influence of previous corrosion on fatigue crack initiation has been determined. Cylindrical specimens and flat specimens with a central hole of the aluminium alloy T075-T6 were corroded in a 3.5 % NaC1 solution. The cylindrical specimens were tested under constant amplitude loading while for the specimens with a central hole a block...