A site-sensitive quasi-in situ strategy to characterize Mo/HZSM-5 during activation

The active sites on the methane dehydroaromatization (MDA) catalyst Mo/HZSM-5 are very hard to characterize, because they are present in various geometries and sizes and only form under reaction conditions with methane at 700 °C. To address these issues an experimental strategy is presented that enables distinguishing different active sites...

Structure-activity relationships in metal organic framework derived mesoporous nitrogen-doped carbon containing atomically dispersed iron sites for CO₂ electrochemical reduction

Mesoporous nitrogen-doped carbon nanoparticles with atomically dispersed iron sites (named mesoNC-Fe) are synthesized via high-temperature pyrolysis of an Fe containing ZIF-8 MOF. Hydrolysis of tetramethyl orthosilicate (TMOS) in the MOF framework prior to pyrolysis plays an essential role in maintaining a high surface area during the...

Metal-Organic-Framework-Mediated Nitrogen-Doped Carbon for CO₂ Electrochemical Reduction

A nitrogen-doped carbon was synthesized through the pyrolysis of the well-known metal-organic framework ZIF-8, followed by a subsequent acid treatment, and has been applied as a catalyst in the electrochemical reduction of carbon dioxide. The resulting electrode shows Faradaic efficiencies to carbon monoxide as high as ∼78%, with hydrogen...

On the dynamic nature of Mo sites for methane dehydroaromatization

The mechanism of methane activation on Mo/HZSM-5 is not yet fully understood, despite the great interest in methane dehydroaromatization (MDA) to replace aromatics production in oil refineries. It is difficult to assess the exact nature of the active site due to fast coking. By pre-carburizing Mo/HZSM-5 with carbon monoxide (CO), the MDA active...

Manufacture of highly loaded silica-supported cobalt Fischer-Tropsch catalysts from a metal organic framework

The development of synthetic protocols for the preparation of highly loaded metal nanoparticle-supported catalysts has received a great deal of attention over the last few decades. Independently controlling metal loading, nanoparticle size, distribution, and accessibility has proven challenging because of the clear interdependence between...