Influence of fiber orientation on the mechanical responses of engineering cementitious composite (ECC) under various loading conditions

The mechanical performance of engineered cementitious composite (ECC) depends greatly on fiber orientation and distribution. In this paper, the effect of fiber orientation on ECC's mechanical properties was investigated using two different casting methods: a flow-induced casting was used to enhance the fiber orientation within ECC mixture and...

Chloride penetration resistance of engineered cementitious composite (ECC) subjected to sustained flexural loading

This paper presents a research on the chloride penetration behavior of engineered cementitious composites (ECC) under sustained flexural loads. Three load levels, i.e. 30 %, 60 % and 75 % of the ultimate flexural load were used. Chloride diffusion depth and concentration profile were measured 30, 60 and 150 days after the specimen was exposed...

Behavior of Engineered Cementitious Composites (ECCs) Subjected to Coupled Sustained Flexural Load and Salt Frost

The performance of engineered cementitious composites (ECCs) under coupled salt freezing and loaded conditions is important for its application on the transportation infrastructure. However, in most of the studies, the specimens were generally loaded prior to the freezing. The influence of sustained load was merely considered. To this end,...

Carbonation Behavior of Engineered Cementitious Composites under Coupled Sustained Flexural Load and Accelerated Carbonation

Engineered cementitious composites (ECCs) belong to a broad class of fibre-reinforced concrete. They incorporate synthetic polyvinyl alcohol (PVA) fibres, cement, fly ash and fine aggregates, and are designed to have a tensile strain capacity typically beyond 3%. This paper presents an investigation on the carbonation behaviour of engineered...

An Interface Co-modification Strategy for Improving the Efficiency and Stability of CsPbI₃Perovskite Solar Cells

Interface engineering is a simple and effective strategy for improving the photovoltaic performance and stability of perovskite solar cells (PSCs). Herein, an interface co-modification strategy is proposed, using [6,6]-phenyl-C61-butyric acid methyl ester (PCBM) and 2-fluoro-1,4-phenylenediammonium iodide (2FPPD) to modify the electron...

Effect of crack width and wet-dry cycles on the chloride penetration resistance of engineered cementitious composite (ECC)

The resistance of cracked ECC against chloride ingress is mainly governed by the accumulated crack width of all the cracks rather than the maximum width of multiple cracks. However, most studies focus on the influence of a single fine crack

Fatigue life and cracking characterization of engineered cementitious composites (ECC) under flexural cyclic load

This paper presents a study on cracking characterization of engineered cementitious composites (ECC) under flexural cyclic load using digital image correlation (DIC) technique. Five stress levels, namely 0.65, 0.75, 0.8, 0.85 and 0.9 of the flexural strength, were applied. Strain map at the side surface was obtained by DIC and used to drive...