- document
-
de Jonge, J.B. (author)The paper starts with a general discussion on various aspects of life re-assessment. Specific attention is paid to the possibility of re-assesgrnent by means of comparative fatigue tests on specimens. As an illustration of this method, the paper gives a description of the life-re-assessment procedures applied by the Royal Netherlands Airforce...report 1979
- document
-
de Jonge, J.B. (author)Fokker-VFW is carrying out a completely new fatigue evaluation of the F-2T aircraft, covering lives up to 120000 flights. This evaluation includes; a)A complete inventory of the configuration status of the F-2T fleet, b)An inventory and evaluation of existing test experience, c)Evaluation of service experience, d)Analytical predictions of life...report 1978
- document
-
Wanhill, R.J.H. (author)Fracture toughness tests on two high strength titanium alloys, IMI 550 and 551, showed that the higher strength alloy, IMI 551, had a much lower toughness. The alloys were very similar in microstructure and fracture mechanisms. A number of model formulations for predicting fracture toughness were compared with the experimental results. This...report 1978
- document
-
de Graaf, E.A.B. (author), de Rijk, P. (author)The present report describes how fatigue cracks were produced in 102 specimens. After cracking these specimens were inspected non-destructively by means of eddy currents, ultrasonics. X-rays and penetrants, and the indications were recorded. Successively the specimens were exposed to corrosion whereafter the inspections were repeated. Upon...report 1978
- document
-
Schijve, J. (author), Jacons, F.A. (author), Meulman, A.E. (author)Flight simulation tests on 2024-T3 and 7075-T6 lug specimens indicated significant fatigue life improvements obtained by expanding the holes in accordance with the split-sleeve cold work method. Geometrical distortions induced by the expansion were measured. The significance of residual stresses is analysed with reference to depth of penetration...report 1978
- document
-
Wanhill, R.J.H. (author)Flight simulation fatigue crack propagation tests with gust spectrum loading were carried out on 2024-T3/carbon-epoxy, 7475-T76l/carbon-epoxy and Ti-6Al-4V/carbon-epoxy laminates with nominal weight savings of -30% as compared to equivalent 2024-T3 panels. The performance of the 2024-T3/carbon-epoxy laminates was much superior to those of the...report 1978
- document
-
de Jonge, J.B. (author), Nederveen, A. (author), Tromp, P.J. (author)Riveted specimens that are considered representative for F-27 type wing structure were subjected to comparative flight simululation test in which the gust load severity and Ground-Air-Ground cycle were systematically varied. The effect of these variations on crack propagation behaviour was studied by means of crack growth tests on 2 mm sheet...report 1978
- document
-
de Jonge, J.B. (author), Nederveen, A. (author), Tromp, P.J. (author)Fatigue tests under flight simulation loading were done on simple notched 2024-T3 Alclad sheet specimens. Reduction of the gust load amplitudes resulted in an increase of crack initiation life but hardly influenced crack propagation. Reduction of the overall stress level increased both initiation and crack propagation life. The observed...report 1978
- document
-
Wanhill, R.J.H. (author)2024-T3, 2048-T851, 7075-T6 and 7475-T761 aluminium alloy sheets were compared for fatigue crack propagation resistance under manoeuvre spectrum and constant amplitude loading. For manoeuvre spectrum loading 7475-T761 was superior overall, and this superiority is most probably due to superior toughness of this alloy. In more detail, 2024-T3 was...report 1978
- document
- Wanhill, R.J.H. (author) report 1978
- document
-
't Hart, W.G.J. (author)Residual strength tests have been carried out on various Kevlar 49-Carbon epoxy laminate configurations consisting of a carbon/epoxy core with face sheets of Kevlar 49 fabric. The influence of fatigue loading of notched specimens on the residual strength was investigated.report 1978
- document
- Wanhill, R.J.H. (author), Döker, H. (author) report 1977
- document
-
Schra, L. (author), van Leeuwen, H.P. (author)The influence of previous corrosion on the fatigue life was investigated. It was foimd that a slight corrosive attack could drastically reduce the fatigue life. The damaging effect of corrosion was greater for the alloy AA 7050 than for AZ 74.61. It could be established that fatigue cracks initiated from various corrosion pits. A second series...report 1977
- document
-
de Rijk, P. (author), Schijve, J. (author)A second series of exploratory acoustic fatigue tests using a shaker. A second series of exploratory acoustic fatigue tests was carried out, again employing simple specimens mounted on a shaker. Strain measurements were compared with calculations. Crack growth initiated by a central notch was observed. A comparison was made between three types...report 1977
- document
- 't Hart, W.G.J. (author) report 1977
- document
-
Wanhill, R.J.H. (author)Plight simulation fatigue crack propagation tests with gust spectrum loading were carried out on 2024-T3/carbon-epoxy, 7475-T761/carbon-epoxy and Ti-6Al-4V/carbon-epoxy laminates with nominal weight savings of 30% as compared to equivalent 2024-T3 panels. The performance of the 2024-T3/ carbon-epoxy laminates was much superior to those of the...report 1977
- document
- Wanhill, R.J.H. (author) report 1977
- document
-
van Gestel, G.F.J.A. (author)In this report an attempt is made to give an overview of the various aspects involved in a fracture surface investigation, stating with a definition of fractography and why it is done. Then the equipment needed is discussed, including stereo-microscopes, optical microscopes, transmission and scanning electron microscopes, and micro-analysis...report 1977
- document
-
Schijve, J. (author), Jacobs, F.A. (author), Tromp, P.J. (author)Comparative flight-simulation tests on four types of joints of 2024- T3 sheet material were carried out with and without application of the penetrant LPS-3. Types of joints were douhle strap joint with hi-lok bolts, asymmetric strap joint, lap joint with countersunk rivets and lap joint with dimpled holes. Observations on slip during the fatigue...report 1977
- document
-
Wanhill, R.J.H. (author)This paper concisely reviews and discusses (1) metallurgically cleaner alloys like -2124, 2048 and 7475, (2) potential application of 7000 series alloys in tension panels, (3) development of high strength stress corrosion resistant thick section materials like 7010, 7049 and 705O, (4) powder metallurgy 7000 series alloys with high strength and...report 1977