Self healing of creep damage in iron-based alloys by supersaturated tungsten

When metals are mechanically loaded at elevated temperatures for extended periods of time, creep damage will occur in the form of cavities at grain boundaries. In the present experiments it is demonstrated that in binary iron-tungsten alloys creep damage can be self healed by selective precipitation of a W-rich phase inside these cavities. Using...

Microstructural evolution of white and brown etching layers in pearlitic rail steels

The formation of White (WEL) and Brown Etching Layers (BEL) on rail raceways during service causes the initiation of microcracks which finally leads to failure. Detailed characterization of the WEL and the BEL in a pearlitic rail steel is carried out from micrometer to atomic scale to understand their microstructural evolution. A...

Atomic-scale investigations of isothermally formed bainite microstructures in 51CrV4 spring steel

Atomic-scale investigation was performed on 51CrV4 steel, isothermally held at different temperatures within the bainitic temperature range. Transmission electron microscopy (TEM) analysis revealed three different morphologies: lower, upper, and inverse bainite. Atom Probe Tomography (APT) analysis of lower bainite revealed cementite...

Micro fracture investigations of white etching layers

The fracture behavior of a white etching layer formed on the rail surface in pearlitic steels during the rail-wheel contact is investigated using indentation-based microcantilever fracture tests. The sample thickness is in the order of 5 μm. The local fracture toughness of the white etching layer, its neighboring brown etching layer, martensite...