Garbatov, Y. (author), Ås, S.K. (author), Branner, Kim (author), Choi, B.K. (author), den Besten, J.H. (author), Dong, P. (author), Lillemäe, I. (author), Lindstrom, P. (author), Lourenço de Souz, M. (author), Parmentier, G. (author), Quéméner, Y. (author), Rizzo, C.M. (author), Rörup, J. (author), Vhanmane, Suhas (author), Villavicencio, R. (author), Wang, F. (author), Yuan, Yue (author)Concern for crack initiation and growth under cyclic loading as well as unstable crack propagation and tearing in the ship and offshore structures. Due attention shall be paid to the suitability and uncertainty of physical models and testing. Consideration is to be given to practical application, statistical description and fracture control...conference paper 2018
- document
-
Schijve, J. (author), Jacobs, F.A. (author)Several simple crack stopping methods were evaluated In fatigue crack propagation tests on 2024-T3 Alclad sheet specimens. After precracklng until a crack of 40 mm was obtained crack stoppers were Installed and the fatigue test was continued. Crack stoppers Installed In stop holes were: a blind rivet, a hard driven rivet, a heavily tightened...report 1984
- document
-
de Graaf, E.A.B. (author), de Rijk, P. (author)The present report describes how fatigue cracks were produced in 102 specimens. After cracking these specimens were inspected non-destructively by means of eddy currents, ultrasonics. X-rays and penetrants, and the indications were recorded. Successively the specimens were exposed to corrosion whereafter the inspections were repeated. Upon...report 1978
- document
-
de Jonge, J.B. (author), Nederveen, A. (author), Tromp, P.J. (author)Fatigue tests under flight simulation loading were done on simple notched 2024-T3 Alclad sheet specimens. Reduction of the gust load amplitudes resulted in an increase of crack initiation life but hardly influenced crack propagation. Reduction of the overall stress level increased both initiation and crack propagation life. The observed...report 1978