Experimental evaluation of interface adhesion of a flax fiber composite patch with epoxy and polyurethane adhesives for the reinforcement of steel structures

Using fiber-reinforced composite patches for repairing damaged structures made of metal or/and concrete is an interesting and widely available solution on the market using synthetic materials. These repairing patches are bonded on the structures’ surfaces to increase their strength against internal stresses, as well as protect them from external...

Understanding fracture mode-mixity and its effects on bond performance

This chapter discusses the mixed-mode loading of adhesive joints. The importance of mixed-mode loading is first introduced and then test methods commonly used to measure the mixed-mode fracture resistance of adhesive joints are presented and briefly discussed. The approaches to determine the fracture resistance are briefly reviewed and then...

Structural integrity assessment of a full-scale adhesively-bonded bi-material joint for maritime applications

The present study proposes a comprehensive integrity assessment approach for a full-scale adhesively-bonded bi-material joint for maritime applications. The joint represents a cross-section of the bond-line connection of a ship with a steel hull and a sandwich composite superstructure. The full-scale joint consists of a sandwich composite...

A review of experimental and theoretical fracture characterization of bi-material bonded joints

High performance structures require the use of different materials to meet their demanding requirements. Especially fibre reinforced polymer composites are nowadays often bonded to metals in order to take the most advantage of the materials properties and to minimize their disadvantages. However, the interface in such bi-material assemblies...

Testing mechanical performance of adhesively bonded composite joints in engineering applications: an overview

The development of new adhesives has allowed to expand the application of bonding into the most diverse industrial fields. This review article presents the commonly used experimental methods for the investigation of mechanical performance of adhesively bonded joints in the aerospace, wind energy, automotive and civil engineering sectors. In...

Evaluation of the strain-based partitioning method for mixed-mode I+II fracture of bi-material cracks

The goal of this paper is to evaluate the strain-based partitioning method (SBM), an analytical method based on beam analysis, for the mixed-mode fracture characterization of asymmetric cracks. The fracture energy is calculated at the crack tip of mixed-mode bending (MMB) test with asymmetric geometry and asymmetric material parameters. The...

Effect of salt spray ageing on the fracture of composite-to-metal bonded joints

This work investigates the effect of long-term environmental exposure on the performance of composite-to-metal bonded joints. Specimens are manufactured using a carbon-fiber reinforced polymer (CFRP) co-bonded to a steel member with epoxy adhesive and aged in a salt spray chamber. The mixed-mode fracture behavior of the non-aged and aged...

Damage assessment of a titanium skin adhesively bonded to carbon fiber–reinforced plastic omega stringers using acoustic emission

This study is devoted to the use of acoustic emission technique for a comprehensive damage assessment, that is, damage detection, localization, and classification, of an aeronautical metal-to-composite bonded panel. The structure comprised a titanium panel adhesively bonded to carbon fiber–reinforced plastic omega stringers. The panel contained...

On the influence of glass fiber mat on the mixed-mode fracture of composite-to-metal bonded joints

In this work, the influence of a layer of glass fiber mat (GFM) inserted in a bi-material bonded joint interface is investigated as a toughening mechanism to improve the fracture performance of bonded structures. Composite-to-metal bonded specimens were manufactured by hand lay-up using two different consolidation processes: at room pressure...

Role of adherend material on the fracture of bi-material composite bonded joints

The aim of this study is to investigate the effect of the adherend material on the mode I fracture behaviour of bi-material composite bonded joints. Both single-material (steel-steel and composite-composite) and bi-material (steel-composite) joints bonded with a structural epoxy adhesive are studied. Additionally, two adhesive bondline...

Surface pretreatments on CFRP and titanium for manufacturing adhesively bonded bi-material joints

Adhesive bonding is a highly desirable joining technique to join composites to metals. The surfaces of both composite and metal substrates have to be carefully treated before bonding them together, in order to avoid interface failure between the adherend's surface and adhesive. This paper describes the surface pretreatments on carbon fiber...

On the fracture behaviour of CFRP bonded joints under mode I loading: Effect of supporting carrier and interface contamination

This paper addresses the fracture behaviour of bonded composite plates featuring a kissing bond along the crack growth path. Double cantilever beam (DCB) experiments are carried out under a displacement controlled loading condition to acquire the load response. The experimental data are collected and analysed analytically for specimens with...