Salt crystallization is a major cause of damage in porous building materials. Accelerated salt weathering tests carried out in the laboratory are among the most common methods to assess the durability of material to salt decay. However, existing standards and recommendations for salt weathering tests have limitations in terms of effectiveness and/or reliability. In the framework of the RILEM Technical Committee 271-ASC, a procedure has been developed which proposes a new approach to salt crystallization tests. It starts from the consideration that salt damage can be seen as a process developing in two phases: accumulation of the salt in the material and propagation of the decay. In the first phase, salts are introduced in the material and accumulate close to the evaporation surface, while in the second phase damage propagates because of repeated dissolution and crystallization cycles, induced by re-wetting with liquid water and by relative humidity changes. In this paper, the procedure is described and the results of a first round robin validation of the test, carried out on 7 materials and involving 10 laboratories, are presented. The results show that the procedure is effective to cause decay within the time period of the test (about 3 months) and that the decay increases with subsequent cycles. The decay observed differs in type and severity depending on the salt type and concentration and on the type of substrate. The decay types detected in the laboratories are generally representative of those observed in the field for the selected substrates. The differences in durability between the various substrates, as assessed at the end of the test, are in line with the durability expected based on field observation. The reproducibility of the results in terms of decay type is good; some differences have been observed in terms of material loss. These are more significant in the case of NaCl contaminated specimens. Based on the results, proposals for fine-tuning of the procedure are given.

The RILEM TC ASC-271 is developing a new laboratory test to assess the durability of porous building materials to salt crystallisation. The test encompasses two phases: salt accumulation and damage propagation. This paper focuses on designing a procedure for the accumulation phase; this is considered successful when salts crystallise at the material's evaporative surface (common situation observed on site) without the occurrence of damage. Two procedures were developed and tested on two limestones with different porosity: (1) capillary absorption of a salt solution followed by drying, and (2) continuous capillary absorption. Sodium chloride or sodium sulphate solutions were used. Several methods for assessing the salt distribution were employed: ultrasonic pulse velocity, drilling/scratching resistance, hygroscopic moisture content, ion chromatography, scanning electron microscopy, and micro X-ray fluorescence. The results enabled the selection of the most effective protocol for the salt accumulation phase.

The durability of building materials with respect to salt crystallization is commonly determined by accelerated weathering tests, carried out in the laboratory. An effective laboratory weathering test should assess the durability and, in the case of conservation of historic buildings, the compatibility of repair materials with those existing. Besides, the test should provide reliable results within a reasonable period of time, accelerating the deterioration process without however altering its mechanism. Despite several national and international standards, recommendations and guidelines, a commonly accepted testing protocol does not yet exist. Researchers often develop and apply their own procedure, a fact that complicates comparison between different studies. The RILEM Technical Committee 271 ASC has been set up with the scope of developing improved test procedures for the assessment of the behaviour of materials under the influence of salt crystallization, which should overcome the limitations of existing standards and recommendations. This paper constitutes one of the first results of the work of the Technical Committee. It critically reviews the literature on salt crystallization tests, identifies advantages and limitations of the several test protocols and provides new ideas for the development of improved salt crystallization procedures.