Structures fabricated using focused electron beam-induced deposition (FEBID) have sloped sidewalls because of the very nature of the deposition process. For applications this is highly undesirable, especially when neighboring structures are interconnected. A new technique combining FEBID and focused electron beam-induced etching (FEBIE) has been developed to fabricate structures with vertical sidewalls. The sidewalls of carbon FEBID structures have been modified by etching with water and it is shown, using transmission electron microscopy imaging, that the sidewall angle can be tuned from outward to inward by controlling the etch position on the sidewall. A surprising under-etching due to the emission of secondary electrons from the deposit was observed, which was not indicated by a simple model based on etching. An analytical model was developed to include continued etching once the deposit has been removed at the exposed pixel. At this stage the secondary electrons from the substrate then cause the adsorbed water molecules to become effective in etching the deposit from below, resulting in under-etched structures. The evolution of the sidewall angle during etching has also been experimentally observed in a scanning electron microscope by continuously monitoring the secondary electron detector signal.

High resolution dense lines patterned by focused electron beam-induced deposition (FEBID) have been demonstrated to be promising for lithography. One of the challenges is the presence of interconnecting material, which is often carbonaceous, between the lines as a result of the Gaussian line profile. We demonstrate the use of focused electron beam-induced etching (FEBIE) as a scanning electron microscope (SEM)-based direct-write technique for the removal of this interconnecting material, which can be implemented without removing the sample from the SEM for post processing. Secondary electron (SE) imaging has been used to monitor the FEBIE process, and atomic force microscopy (AFM) measurements confirm the fabrication of well separated FEBID lines. We further demonstrate the application of this technique for removing interconnecting material in high resolution dense lines using backscattered electron (BSE) imaging to monitor the process.