In order to reveal more information and better understanding on the behavior and failure mechanisms of high strength steel (HSS) extended endplate connections at ambient temperature and after fire, an experimental and theoretical study has been conducted and presented in this paper. The provisions of Eurocode 3 are verified with the test results. Because strength of bolts decreases more rapidly than that of structural steels, failure modes of endplate connections may change after fire. Hence, a series of equations are proposed to predict failure modes of endplate connections after fire. Furthermore, FE simulations which can predicate the performance of HSS extended endplate connections with reasonable accuracy are adopted to study the behaviors of the connections after cooling down from various fire temperatures and to validate the accuracy of the proposed equations. Moreover, a parametric study is carried out to explore an optimization design method. It is found that the current provisions of EC3 can justifiably predict failure modes and plastic flexural resistances of HSS extended endplate connections both at ambient temperature and cooling down from 550 °C, but it is not the case for their initial rotational stiffness and rotation capacity. In order to avoid brittle failure mode of endplate connections after fire, appropriately increasing the diameter or grade of bolts in the design is suggested. What is more, the match of steel grade and thickness of column flange and endplate as well as beam should be considered in the optimization design of beam-column endplate connections.

Full-scale experimental study and numerical analysis on behaviors and failure mechanisms of full high strength steel extended endplate connections in fire have been carried out and presented in this paper. The experimental behaviors of the connections were compared with the provisions of Eurocode 3. The test results show that the failure modes of the connections in fire are bolt failure with yielding of the flange, as same as those at ambient temperature. The failures of the bolts in fire are ductile while they are brittle at ambient temperature. The rotation capacity of the connections in fire is proved sufficient. What is more, at elevated temperature 550 °C, the plastic moment resistances of Q690 and Q960 full high strength steel endplate connections are only 40% of those at ambient temperature, while their initial rotation stiffness are 66 and 63% respectively. But the rotation capacities of Q690 and Q960 high strength steel endplate connections are 1.38 and 1.74 times of those at ambient temperature. Moreover, it is found that the component method Eurocode 3 proposed based on connections made of mild steels can be used to calculate plastic resistances and to predict failure modes of high strength steel endplate connections in fire, but it is not suitable to predict their stiffness. The suggestions about rotation capacity of connections in Eurocode 3 are found too conservative for high strength steel endplate connections in fire.