Two types of austenite morphologies, equiaxed and Widmanstätten, were produced through different phase transformation routes to evaluate the critical factors affecting the intergranular corrosion susceptibility in a 2205 duplex stainless steel. These distinct austenite morphologies behaved quite differently in secondary phase precipitation on exposure to sensitization temperature. Although the Widmanstätten microstructure was found to have a larger degree of coherent ferrite/austenite interface area compared with the equiaxed one, it showed a higher degree of sensitization. It was clarified that, in addition to the ferrite/austenite interface coherency, the extent of an interface area and presence of un-stable ferrite also play prominent roles in intergranular corrosion susceptibility.

This work investigates the synergetic effect of zinc aluminum polyphosphate (ZAPP) and 2-mercaptobenzimidazole (MBI) on the corrosion protection of mild steel coated with a solvent-borne epoxy-polyamide layer. The magnitude and trend of electrochemical impedance spectroscopy data over 70-d immersion in 3.5 wt.% NaCl solution indicate superior corrosion protection of the combined inhibitors compared to those containing either just ZAPP or MBI. Pull-off tests show that the combined inhibitor system provides an improved adhesion strength. The enhanced corrosion performance is correlated to precipitation of a protective layer at the coating/metal interface verified by SEM and electrochemical studies upon exposure to electrolytes.