Accurate monitoring of physiological temperature is important for many biomedical applications, including monitoring of core body temperature, detecting tissue pathologies, and evaluating surgical procedures involving thermal treatment such as hyperthermia therapy and tissue ablation. Many of these applications can benefit from replacing external temperature probes with injectable wireless devices. Here we present such a device for real-time in vivo temperature monitoring that relies on 'chip-as-system' integration. With an on-chip piezoelectric transducer and measuring only 380 μm × 300 μm × 570 μm, the 0.065-mm ³ monolithic device, in the form of a mote, harvests ultrasound energy for power and transmits temperature data through acoustic backscattering. Containing a low-power temperature sensor implemented with a subthreshold oscillator and consuming 0.813 nW at 37 °C, the mote achieves line sensitivity of 0.088 °C/V, temperature error of +0.22/-0.28 °C, and a resolution of 0.0078 °C rms. A long-term measurement with the mote reveals an Allan deviation floor of <138.6 ppm, indicating the feasibility of using the mote for continuous physiological temperature monitoring.

The atomic-level study of point defect evolution in nuclear graphite is essential for a deep understanding of irradiation-induced property changes. The evolution of helium ion irradiation-induced point defects and helium retention in nuclear graphite ETU-10 and ETU-15 were studied by positron annihilation Doppler broadening (PADB) experiments and thermal desorption spectroscopy (TDS) measurements. The graphite samples were implanted with 10¹⁵, 10^16_, and 10¹⁷ cm⁻² of 200 keV He⁺ at operation temperatures below 373 K. Frenkel pairs were created during ion irradiation and they annihilated during annealing. Three stages of interstitial-monovacancy annihilation are suggested. At low temperatures, the initial annihilation would be refined only to the recombination of intimate metastable Frenkel pairs. When temperature increases, the annihilation would expand to a larger extent that isolate interstitials and vacancies annihilate with each other. In the case of high doses irradiation, vacancy clusters form at elevated temperatures. The retention and release of helium is tightly related to the evolution of the defects, especially the vacancies. The small over-pressured He-V clusters (He_nV) are thought to be the most possible form of helium retention under irradiation.