The anodising process parameters (voltage, temperature, and electrolyte) control the morphology and the chemical composition of the resulting anodic oxide film by altering the balance between oxide growth and oxide dissolution reactions. The porosity of the oxide film is reduced by the addition of tartaric acid to a sulfuric acid electrolyte, while anodising at elevated temperatures enhances oxide dissolution, leading to wider pores and rougher surfaces. No significant changes in the oxide chemical composition as a function of anodising parameters was found; in particular, no tartrate incorporation took place. The resistance of uncoated anodic oxide films against aggressive media and galvanic stress as a function of anodising parameters has been studied by electrochemical methods. Anodising in a mixed tartaric and sulfuric acid electrolyte improves the resistance of the anodic oxide against galvanic stress and aggressive media in comparison to sulfuric acid ano-dising processes. However, the corrosion protection performance of the anodic oxide films in com-bination with a corrosion-inhibitor loaded organic coating is not governed by the blank oxide properties but by the adhesion-enhancing morphological features formed during anodising at elevated temperatures at the oxide/coating interface.

The adhesion capabilities of sulfuric acid and tartaric-sulfuric-acid anodic oxide films on cladded AA2024-T3 aluminium substrates have been investigated in a quantitative manner. A relatively simple, versatile and industrially applicable test methodology based on DIN EN ISO 29862 has been used. In addition, the effect of anodising process parameters on the oxide film morphology has been studied and correlated with the adhesion results. The process parameters considered are the chemistry of the acidic pickling pre-treatment step, the addition of tartaric acid to the sulfuric acid electrolyte, the formation voltage, and the electrolyte temperature. The suggested tape peel adhesion test is able to differentiate among pre-treatments and anodising conditions showing a good correlation with the morphological features at the ultimate surface. High peel adhesion strengths are measured when topographies such as pore mouth widening and dissolution-driven roughness take place. These morphologies are typically found in anodic layers formed at elevated electrolyte temperatures. The proposed method can be beneficial for a fast assessment of anodising parameters for good adhesion, which is of special interest for the industrial optimisation of anodising processes.