3D hybrid perovskites (APbX₃) have made a significant impact on the field of optoelectronic materials due to their excellent performance combined with facile solution deposition and up-scalable device fabrication. Nonetheless, these materials suffer from environmental instability. To increase material stability, the organic cation (A) is substituted by the non-volatile cesium cation. However, the desired photoactive cesium lead(II) iodide black phase is metastable in ambient conditions and spontaneously converts into the photo-inactive yellow δ-phase. In this work, the black phase is stabilized by the formation of a quasi-2D perovskite containing a benzothieno[3,2-b]benzothiophene (BTBT) large organic ammonium cation. Thermal analysis shows that degradation of the butylammonium (BA)-based quasi-2D perovskite (BA)₂CsPb₂I₇ sets in at ≈130 °C, while (BTBT)₂CsPb₂I₇ is phase-stable until ≈230 °C. Additionally, the (BTBT)₂CsPb₂I₇ film does not show any sign of degradation after exposure to 77% Relative Humidity in the dark for 152 days, while (BA)₂CsPb₂I₇ degrades in a single day. Photoconductor-type detectors based on (BTBT)₂CsPb₂I₇ demonstrate an increased external quantum efficiency and a similar specific detectivity compared to the BA-based reference detectors. The results demonstrate the utility of employing a BTBT cation within the organic layer of quasi-2D perovskites to significantly enhance the stability while maintaining the optoelectronic performance.

Research into 2D layered hybrid perovskites is on the rise due to the enhanced stability of these materials compared to 3D hybrid perovskites. Recently, interest towards the use of functional organic cations for these materials is increasing. However, a vast amount of the parameter space remains unexplored in multi-layered (n > 1) hybrid perovskites for solar cell applications. Here, we incorporate carbazole derivatives as a proof of concept towards the use of tailored functional molecules in multi-layered perovskites. Films of low-n carbazole containing perovskites show high photoconductivity half-lifetimes. Higher-n (〈n〉 = 40) multi-layered perovskite films possess charge carrier diffusion lengths comparable to MAPI thin films. Solar cells containing these materials have comparable efficiencies to our MAPI and phenethylammonium (PEA)-containing multi-layered perovskite reference devices. Moisture stability tests were performed both at the material and device levels. In comparison to MAPI and PEA-based materials and solar cells, the addition of a small percentage of the carbazole derivative to the perovskite material significantly enhances the moisture stability.