This paper presents the results of an experimental study performed to investigate the effect of activator modulus (SiO2/Na2O) and slag addition on the fresh and hardened properties of alkali-activated fly ash/slag (AAFS) pastes. Four activator moduli (SiO2 /Na2O), i.e., 0.0, 1.0, 1.5, and 2.0, and five slag-to-binder ratios, i.e., 0, 0.3, 0.5, 0.7, 1.0, were used to prepare AAFS mixtures. The setting time, flowability, heat evolution, compressive strength, microstructure, and reaction products of AAFS pastes were studied. The results showed that the activator modulus and slag content had a combined effect on the setting behavior and workability of AAFS mixtures. Both the activator modulus and slag content affected the types of reaction products formed in AAFS. The coexistence of N–A–S–H gel and C–A–S–H gel was identified in AAFS activated with high pH but low SiO2 content (low modulus). C–A–S–H gel had a higher space-filling ability than N–A–S–H gel. Thus, AAFS with higher slag content had a finer pore structure and higher heat release (degree of reaction), corresponding to a higher compressive strength. The dissolution of slag was more pronounced when NaOH (modulus of 0.0) was applied as the activator. The use of Na2SiO3 as activator significantly refined the pores in AAFS by incorporating soluble Si in the activator, while further increasing the modulus from 1.5 to 2.0 prohibited the reaction process of AAFS, resulting in a lower heat release, coarser pore structure, and reduced compressive strength. Therefore, in view of the strength and microstructure, the optimum modulus is 1.5.@en

The production of cement leads to a large amount of CO2 emission. Using industrial waste slag, such as ceramic polishing powder (PP), to replace part of Portland cement can reduce the pollution caused by the cement industry and solid waste disposal. In order to use PP as a replacement for cement, its effects on the properties of cement paste need to be clarified. In this study, the effect of PP on the nucleation and growth of hydrates in cement paste at very early ages was investigated. Quartz was used as a reference. The interactions of their surface with various ions in cement paste solution, which has an important effect on the nucleation and growth of hydrates, were studied by using the zeta potential test. The morphology of the nucleus and crystal of hydrates was investigated by using SEM. The zeta potential measurements showed that the affinity of the surface of PP and quartz to ions in the pore solution of cement paste is similar. The image of SEM indicated that there is also not much difference in the crystallization of hydrates on the surfaces of PP and quartz. These evidences suggested that PP has similar surface charge properties as quartz, and its effects on the properties of cement paste are the same as that of quartz. From the viewpoint of the effect on very early hydration, PP can be used in cement paste, similar to quartz power.@en