O. Yildirim, S. Cornelius, A. Smekhova, M. Butterling, W. Anwand, A. Wagner, C. Bähtz, R. Böttger, K. Potzger
Structural, defect and magnetic properties of the TiO2:Co films are investigated. We varied the maximum Co+-implantation concentration from 0.5 at.% up to 5 at.%. A concentration window, which is considered as a threshold for the formation of metallic secondary phases is found. At this concentration it is also observed that the majority of the dopant atoms are incorporated into the host lattice.
...
Structural, defect and magnetic properties of the TiO2:Co films are investigated. We varied the maximum Co+-implantation concentration from 0.5 at.% up to 5 at.%. A concentration window, which is considered as a threshold for the formation of metallic secondary phases is found. At this concentration it is also observed that the majority of the dopant atoms are incorporated into the host lattice.