We investigate the deformation of a linear viscoelastic compliant coating in a turbulent flow for a wide range of coating parameters. A one-way coupling model is proposed in which the turbulent surface stresses are expressed as a sum of streamwise-travelling waves with amplitudes determined from the stress spectra of the corresponding flow over a rigid wall. The analytically calculated coating deformation is analysed in terms of the root-mean-square (r.m.s.) surface displacement and the corresponding point frequency spectra. The present study systematically investigates the influence of five coating properties namely density, stiffness, thickness, viscoelasticity and compressibility. The surface displacements increase linearly with the fluid/solid density ratio. They are linearly proportional to the coating thickness for thin coatings, while they become independent of the thickness for thick coatings. Very soft coatings show resonant behaviour, but the displacement for stiffer coatings is proportional to the inverse of the shear modulus. The viscoelastic loss angle has only a significant influence when resonances occur in the coating response, while Poisson's ratio has a minor effect for most cases. The modelled surface displacement is qualitatively compared with recent measurements on the deformation of three different coatings in a turbulent boundary-layer flow. The model predicts the order of magnitude of the surface displacement, and it captures the increase of the coating displacement with the Reynolds number and the coating softness. Finally, we propose a scaling that collapses all the experimental data for the r.m.s. of the vertical surface displacement onto a single curve.

The manufacture and preliminary testing of a drag-reducing riblet texture with fouling-control properties is presented. The commercial fouling-release product Intersleek® 1100SR was modified to manufacture riblet-textured coatings with an embossing technology. Hydrodynamic drag measurements in a Taylor–Couette set-up showed that the modified Intersleek® riblets reduced drag by up to 6% compared to a smooth surface. Barnacle settlement assays demonstrated that the riblets did not substantially reduce the ability of Intersleek® 1100SR to prevent fouling by cyprids of Balanus amphitrite. Diatom adhesion tests revealed significantly higher diatom attachment on the riblet surface compared to smooth Intersleek® 1100SR. However, after exposure to flow, the final cell density was similar to the smooth surface. Statically immersed panels in natural seawater showed an increase of biofilm cover due to the riblets. However, the release of semi-natural biofilms grown in a multi-species biofilm culturing reactor was largely unaffected by the presence of a riblet texture.