Durability of photocatalytic coatings is a major concern in engineering practice. Here, two types of novel visible light-responsive coatings, both consisting of vinyl chloride/vinyl ester/ethylene copolymer (as a binder) and graphitic carbon nitride (g-C3N4) but different in fabrication, are proposed and applied on the mortar surface. The first type is mono-layer coating (MC), where the g-C3N4 suspension containing the binder is directly sprayed on the mortar. The second type is double-layer coating (DC), where the binder layer is applied on mortar surface before spraying the g-C3N4 layer. Results show that the binder addition leads to a good anchorage of the coatings on both MC and DC mortar substrates, along with desirable resistance to peeling and washing, compared to the g-C3N4 coated mortar without the binder. The well-distributed binder in g-C3N4-based coating inevitably decreases the photocatalytic efficiency of the MC mortar due to masking effect of the binder on the coating surface. The DC mortar, on the contrary, takes full advantage of the binder adhesion by inserting a binder layer and therefore holds strong resistance to peeling and washing without compromising its photocatalytic efficiency. The proposed DC technique provides a promising strategy to fabricate highly cost-effective and durable photocatalytic coatings applied on cementitious materials.@en

The combination of photocatalyst with cementitious materials for air pollution abatement and self-cleaning has gained considerable attention. However, the most popularly used photocatalytic cementitious composites based on TiO2 achieve the purification function under ultraviolet sunlight, significantly impeding a broader application of photocatalytic cementitious composites. Here, the photocatalytic cementitious composites were prepared by incorporating g-C3N4 nanosheets (CNNs) in Portland cement. With the increase of CNNs content, the photocatalytic NOx abatement and self-cleaning performance was notably improved, while the micro-hardness of cementitious composites increased first and then decreased. Among the three mixing dosages (0.5%, 1% and 2% by weight of cement), the cementitious composite admixed with 2% CNNs showed the highest photocatalytic NOx abatement efficiency of 227.3 μmol m−2 h−1, and could degrade the rhodamine B within 40 min under visible light. Additionally, its microscopic hardness was 5.4% higher than the one without CNNs, suggesting that a moderate amount of CNNs (below 2%) in cementitious composites was effective in achieving an improved photocatalytic depollution performance.@en