To explore the effects of solvent-ionomer interactions in catalyst inks on the structure and performance of Cu catalyst layers (CLs) for CO₂ electrolysis, we used a “like for like” rationale to select acetone and methanol as dispersion solvents with a distinct affinity for the ionomer backbone or sulfonated ionic heads, respectively, of the perfluorinated sulfonic acid (PFSA) ionomer Aquivion. First, we characterized the morphology and wettability of Aquivion films drop-cast from acetone- and methanol-based inks on flat Cu foils and glassy carbons. On a flat surface, the ionomer films cast from the Aquivion and acetone mixture were more continuous and hydrophobic than films cast from methanol-based inks. Our study’s second stage compared the performance of Cu nanoparticle CLs prepared with acetone and methanol on gas diffusion electrodes (GDEs) in a flow cell electrolyzer. The effects of the ionomer-solvent interaction led to a more uniform and flooding-tolerant GDE when acetone was the dispersion solvent (acetone-CL) than when we used methanol (methanol-CL). As a result, acetone-CL yielded a higher selectivity for CO₂ electrolysis to C₂₊ products at high current density, up to 25% greater than methanol-CL at 500 mA cm^-2. Ethylene was the primary product for both CLs, with a Faradaic efficiency for ethylene of 47.4 ± 4.0% on the acetone-CL and that of 37.6 ± 5.5% on the methanol-CL at a current density of 300 mA cm^-2. We attribute the enhanced C₂₊ selectivity of the acetone-CL to this electrode’s better resistance to electrolyte flooding, with zero seepage observed at tested current densities. Our findings reveal the critical role of solvent-ionomer interaction in determining the film structure and hydrophobicity, providing new insights into the CL design for enhanced multicarbon production in high current densities in CO₂ electrolysis processes.

Achieving operational stability at high current densities remains a challenge in CO2 electrolyzers due to flooding of the gas diffusion layer (GDL) that supports the electrocatalyst. We mitigated electrode flooding at high current densities using a vacuum-assisted infiltration method to embed 200-400 nm-sized polytetrafluoroethylene (PTFE) particles at the interface of the microporous layer (MPL) and carbon cloth in a commercial GDL. In CO2 electrolysis to CO over a silver nanoparticle catalyst on the GDL, the PTFE-embedded GDL not only just exhibited less than 10% of the electrolyte seepage rates observed in untreated GDLs at a current density of 300 mA·cm-2 but also expanded the electrochemical active area across the testing conditions. The PTFE-embedded GDL also maintained a Faradaic efficiency for CO2 electrolysis to CO above 80% for more than 100 h at 100 mA·cm-2, which was a 50-fold improvement in the stable operation time of the electrolyzer.