A set of doped iron oxides (chromium, aluminum, gallium, indium, manganese, zinc, niobium) were prepared by a one-step coprecipitation/calcination approach evaluated for their WGS activity under industrially relevant conditions and characterized in detail. The WGS activity after ageing the doped catalyst for 4 days at 25 bar follows the order chromium ≈ aluminum > gallium > indium > manganese > zinc > niobium for copper-codoped catalysts. The activated catalysts predominantly consist of magnetite, irrespective of the dopant. Mössbauer spectra of aged catalysts showed that aluminum and zinc occupy both tetrahedral and octahedral sites of magnetite, while chromium, gallium, indium, manganese, and niobium preferentially substitute octahedral iron. The incorporation of trivalent metal ions of similar size to octahedral Fe3+ (i.e., chromium, aluminum, gallium) results in moderate to high CO conversion, irrespective of incorporation in tetrahedral or octahedral sites. The substitution of Fe2+ with Mn2+ results in an increased Fe3+/Fe2+ ratio. Incorporation of Zn2+ in tetrahedral sites (replacing Fe3+ ions) leads to a complex structure where the charge balance is compensated from the octahedral sites. Separate dopant metal oxide phases were observed in indium- and niobium-doped catalysts. XPS shows that copper is present as a separate phase in activated copper-codoped catalysts. Aluminum is identified as the most promising promoter for substituting chromium in commercial high-temperature WGS catalysts on the basis of their similar high CO conversion although incorporation of these dopants into the magnetite structure differed substantially. @en

Chromium promotion of iron oxide based water-gas shift (WGS) catalysts prepared via co-precipitation/calcination was investigated. Mössbauer spectroscopy and XRD evidence that chromium is incorporated in the calcined hematite (α-Fe2O3) precursor irrespective of the doping level (0−12 wt.%). CO-TPR shows chromium delays the reduction of hematite and the active magnetite (Fe3O4) phase. WGS activity was evaluated under realistic conditions for 4 days. Enhanced CO conversion was observed with increased chromium doping. Mössbauer spectra indicate that chromium incorporates into octahedral sites of magnetite and prevents reduction of Fe3+ to Fe2+ during formation of the active phase, leading to an increased Fe3+/Fe2+ ratio in octahedral sites. The higher Fe3+/Fe2+ ratio did not affect the high CO conversion associated with the structural stabilization mechanism of Cr-doping. Interpretation of the Mössbauer spectra was supported by computational modelling of various chromium and vacancy-doped magnetite structures. The bulk structure of an in situ prepared chromium-doped high-temperature WGS catalyst is best described as a partially oxidized chromium-doped magnetite phase. No surface effects of Cr-doping were found.@en