Titanium aluminide alloys are considered to be attractive materials for aerospace and automotive high-temperature applications due to their high specific strength, creep resistance, and heat resistance. However, their brittleness makes it difficult to manufacture complex-shaped components of these alloys using conventional processes making additive manufacturing a promising way to produce titanium aluminide parts. Additive manufacturing of titanium aluminide alloys involves high preheating temperatures affecting their microstructure; hence a proper heat treatment is needed to obtain desired properties. In this paper, a titanium aluminide alloy produced using Selective Laser Melting process with a high-temperature preheating was subjected to various heat treatments to study their effects on microstructure and properties of the alloy.

@en

The paper investigates the effect of hot isostatic pressing of single-crystal nickel-based alloy manufactured by selective laser melting (SLM) with a high-temperature substrate preheating. A study of the structure and phase composition of the material before and after treatment has been carried out. It was found that as a result of such treatment, the ratio and proportion of the strengthening phases change; however, due to slow cooling after treatment, the optimal ratio and shape of the inclusions are not fixed. In addition, the hardening particles are precipitated.@en