The formation of a protein nanobiofilm on the surface of degradable biomaterials such as magnesium (Mg) and its alloys influences metal ion release, cell adhesion/spreading, and biocompatibility. During the early stage of human body implantation, competition and interaction between inorganic species and protein molecules result in a complex film containing Mg oxide and a protein layer. This film affects the electrochemical properties of the metal surface, the protein conformational arrangement, and the electronic properties of the protein/Mg oxide interface. In this study, we discuss the impact of various simulated body fluids, including sodium chloride (NaCl), phosphate-buffered saline (PBS), and Hanks' solutions on protein adsorption, electrochemical interactions, and electrical surface potential (ESP) distribution at the adsorbed protein/Mg oxide interface. After 10 min of immersion in NaCl, atomic force microscopy (AFM) and scanning Kelvin probe force microscopy (SKPFM) showed a higher surface roughness related to enhanced degradation and lower ESP distribution on a Mg-based alloy than those in other solutions. Furthermore, adding bovine serum albumin (BSA) to all solutions caused a decline in the total surface roughness and ESP magnitude on the Mg alloy surface, particularly in the NaCl electrolyte. Using SKPFM surface analysis, we detected a protein nanobiofilm (∼10-20 nm) with an aggregated and/or fibrillary morphology only on the Mg surface exposed in Hanks' and PBS solutions; these surfaces had a lower ESP value than the oxide layer.@en

In this paper, different macroscopic electrochemical techniques are applied to study the corrosion inhibitor efficiency, protection mechanism and stability of a calcium aluminum polyphosphate silicate hydrate inhibitor on hot-dip galvanized steel in the time-domain. Potentiodynamic polarization (PP) measurements are applied to study the anodic and cathodic mechanistic behavior as well as inhibitor efficiencies at discrete and single times of exposure. Open circuit potential (OCP) with superimposed linear polarization resistance (LPR) measurements are applied as a faster, non-invasive alternative to PP, characterizing the overall performance of the system in terms of the polarization resistance. Electrochemical impedance spectroscopy (EIS) measurements are applied to detail both the overall performance of the system as well as the corrosion inhibition mechanism related to the electrochemical system’s physicochemical representation over time. Electrochemical noise (EN) measurement are used to evaluate the inhibition efficiency as a function of exposure time, represented by the electrochemical noise resistance. Odd random phase electrochemical impedance spectroscopy (ORP-EIS) is selected as the electrochemical tool to study the system’s instability, by evaluation of the non-linearities and non-stationarities over time. The non-stationarities present in the inhibitor-containing electrochemical system are shown to cause the overall instability of the system and should be taken into account when interpreting results from the different techniques over time.@en