3D printing is a powerful manufacturing technology for shaping materials into complex structures. While the palette of printable materials continues to expand, the rheological and chemical requisites for printing are not always easy to fulfill. Here, a universal manufacturing platform is reported for shaping materials into intricate geometries without the need for their printability, but instead using light-based printed salt structures as leachable molds. The salt structures are printed using photocurable resins loaded with NaCl particles. The printing, debinding, and sintering steps involved in the process are systematically investigated to identify ink formulations enabling the preparation of crack-free salt templates. The experiments reveal that the formation of a load-bearing network of salt particles is essential to prevent cracking of the mold during the process. By infiltrating the sintered salt molds and leaching the template in water, complex-shaped architectures are created from diverse compositions such as biomedical silicone, chocolate, light metals, degradable elastomers, and fiber composites, thus demonstrating the universal, cost-effective, and sustainable nature of this new manufacturing platform.@en

Porosity is an essential feature in a wide range of applications that combine light weight with high surface area and tunable density. Porous materials can be easily prepared with a vast variety of chemistries using the salt-leaching technique. However, this templating approach has so far been limited to the fabrication of structures with random porosity and relatively simple macroscopic shapes. Here, a technique is reported that combines the ease of salt leaching with the complex shaping possibilities given by additive manufacturing (AM). By tuning the composition of surfactant and solvent, the salt-based paste is rheologically engineered and printed via direct ink writing into grid-like structures displaying structured pores that span from the sub-millimeter to the macroscopic scale. As a proof of concept, dried and sintered NaCl templates are infiltrated with magnesium (Mg), which is typically highly challenging to process by conventional AM techniques due to its highly oxidative nature and high vapor pressure. Mg scaffolds with well-controlled, ordered porosity are obtained after salt removal. The tunable mechanical properties and the potential to be predictably bioresorbed by the human body make these Mg scaffolds attractive for biomedical implants and demonstrate the great potential of this additive technique.@en