Electrically active hydrogels are attracting significant interest as biohybrid materials for electrical interfacing with biological tissues. Here, we report the development of electrically active hydrogels, specifically engineered for in vitro neural cell cultures. The hydrogels’ matrix comprises a viscoelastic alginate primary network, interpenetrated by a secondary network formed by the neural cell-adhesive protein, laminin. Conducting poly(3,4-ethylenedioxythiophene):polystyrene sulfonate (PEDOT:PSS) particles are embedded throughout the hydrogel matrix, serving as the electrically active filler phase. Oscillatory rheology confirmed the viscoelastic nature of the composite hydrogels, with storage and loss moduli in the range of 1–10 kPa, suitable for neural tissue interfacing. The hydrogels exhibited high optical transparency across the visible spectrum. At a wavelength of 500 nm, transmission exceeded 45% for 400 µm thick hydrogels and was further enhanced to over 60% by reducing the hydrogel thickness to 150 µm. We established a reproducible protocol for electrochemical impedance spectroscopy and cyclic voltammetry measurements, demonstrating that the incorporation of PEDOT:PSS significantly enhanced both conductivity and charge storage capacitance of hydrogel films. The alginate–laminin–PEDOT:PSS hydrogels demonstrated excellent operational stability, maintaining consistent electrochemical performance over 80 charging/discharging cycles and remaining structurally and functionally stable under cell culture conditions for over four weeks. Cortical neuron cultures derived from human induced pluripotent stem cells prove the stability and cytocompatibility of our proposed hydrogels for over 28 days in culture. Collectively, these results highlight the potential of electrically active hydrogels loaded with PEDOT:PSS as soft, bioelectronic interfaces for neural engineering applications.

Osteoporosis is the most widespread metabolic bone disease which represents a major public health burden. Consequently, novel biomaterials with a strong capacity to regenerate osteoporotic bone defects are urgently required. In view of the anti-osteoporotic and osteopromotive efficacy of alendronate and 45S5 bioactive glass, respectively, we investigated the feasibility to synthesize novel hybrid particles by exploiting the strong interactions between these two compounds. Herein, we demonstrate the facile preparation of a novel class of hybrid particles of tunable morphology, chemical composition and structure. These hybrid particles (i) release alendronate and various inorganic elements (Ca, Na, Si, and P) in a controlled manner, (ii) exhibit a strong anti-osteoclastic effect in vitro, and (iii) stimulate regeneration of osteoporotic bone in vivo. Consequently, this novel class of hybrid biomaterials opens up new avenues of research on the design of bone substitutes with specific activity to facilitate regeneration of bone defects in osteoporotic patients.