The phenomena of constituent redistribution, wherein a previously homogeneous metallic fuel forms discrete, radially concentric compositional zones upon irradiation was investigated by examining an irradiated U-19Pu-14Zr fuel (where numbers represent wt. %) with a burnup of 11.5 at.% with electron probe microanalysis (EPMA) and quadruple inductively coupled plasma mass spectroscopy (Q-ICP-MS).

EPMA-generated U, Pu, and Zr compositional data obtained from a diameter traverse of the sample was converted to mass and was used to: 1) compare the overall fuel element analysis results between the two methods, 2) determine the number of compositionally distinct zones forming as a result of constituent redistribution; and 3) quantify the post-irradiation loss or gain of U, Pu, and Zr atoms in each distinct compositional zone.

Weight percent concentrations of U, Pu, and Zr for the overall cross section compare favorably between the two analytical methods, suggesting that the spatially resolved EPMA analysis complements bulk chemical analysis.

Among the four identified compositional zones, post-irradiation quantification of U, Pu, and Zr elemental atom content changes shows that the quantity of U atoms lost from the innermost zone is slightly less than the quantity of U atoms gained by the middle two zones, and the quantity of Zr atoms lost from the high-U third zone is slightly less than is gained by the two innermost zones. Pu is lost from all four zones, although the innermost zone and the high-U third zone lose a significantly higher percentage (> 22 %) of their initial Pu atoms than the other two zones. For all three elements, EPMA cannot distinguish between atoms lost due to transport to a different zone from atoms lost due to nuclear processes; however, the insight gained from using this process can be used to experiment with new modeling techniques to predict constituent redistribution in U-Pu-Zr fuels.@en

Two irradiated AGR-2 TRISO particles were chosen to demonstrate a recently developed mass balance technique in which EPMA-generated concentration data were used to determine fission product mass on a layer-by-layer basis in TRISO particles. EPMA-calculated fission product masses for most fission products in the two particles were within ± 20% of their ORIGEN-modelled masses. Results show that Sr, Ba, and Eu accumulate preferentially in the carbon-rich kernel periphery on the particles’ side that lacks a gap between the buffer and IPyC. In addition, the more mobile elements—Cs, Sr, Pd, and Ag, accumulate in greater quantity in the outer layers of particle AGR2-223-RS34 compared to particle AGR2-223-RS06, which has relatively more of those elements’ mass located in the kernel and kernel periphery, suggesting enhanced fission product transport in particle AGR2-223-RS34. This model can be used better understand and test fission product transport in TRISO particles. Graphical abstract: [Figure not available: see fulltext.]

@en

Two tristructural isotropic (TRISO)-coated nuclear fuel particles were examined by electron probe microanalysis (EPMA) as part of the Advanced Gas Reactor program. The compacts’ average irradiation temperatures ranged from approximately 1260 to 1290 °C. One particle was examined in the as-irradiated condition, while the other was subject to 1600 °C post-irradiation safety testing. This study was undertaken to test a newly-developed EPMA technique to determine fission product masses in TRISO particles on a layer-by-layer basis, and to compare fission product distributions between an as-irradiated and safety-tested particle. Fission product concentration profiles were collected along two radii in each particle, with measured concentrations used to compute the fission product mass in each TRISO particle layer. These measured masses were then compared to those predicted from ORIGEN modeling calculations. Data collected from these measurements show that for these two particles, masses determined via EPMA were within ± 20% of the calculated masses for the rare-earth elements, Mo, Zr, Cs, I, and Pd. Elements that tend to be less homogeneously distributed include Sr, Te, Eu, Ag, and possibly Ba. Measured Ag masses differed by more than 40% from the calculated mass. Lanthanides other than Eu remain primarily within the fuel kernel in the as-irradiated particle but in the safety-tested particle these element masses were divided approximately equally between the kernel and kernel periphery. In both particles, the majority of Sr and Eu accumulated in the carbon-rich kernel periphery, although in the safety-tested particle, Sr and Eu accumulated farther from the fuel kernel than occurred with irradiation alone. A greater mass fraction of mobile elements, such as Cs and I accumulated in the buffer and IPyC in the safety-tested particle as compared to the as-irradiated particle. When fully developed and tested, this mass balance approach to TRISO particle analysis has the potential to provide insight into fuel behavior.

@en