Unlike metals where dislocations carry strain singularity but no charge, dislocations in oxide ceramics are characterized by both a strain field and a local charge with a compensating charge envelope. Oxide ceramics with their deliberate engineering and manipulation are pivotal in numerous modern technologies such as semiconductors, superconductors, solar cells, and ferroics. Dislocations facilitate plastic deformation in metals and lead to a monotonous increase in the strength of metallic materials in accordance with the widely recognized Taylor hardening law. However, achieving the objective of tailoring the functionality of oxide ceramics by dislocation density still remains elusive. Here a strategy to imprint dislocations with {100}<100> slip systems and a tenfold change in dislocation density of BaTiO₃ single crystals using high-temperature uniaxial compression are reported. Through a dislocation density-based approach, dielectric permittivity, converse piezoelectric coefficient, and alternating current conductivity are tailored, exhibiting a peak at medium dislocation density. Combined with phase-field simulations and domain wall potential energy analyses, the dislocation-density-based design in bulk ferroelectrics is mechanistically rationalized. These findings may provide a new dimension for employing plastic strain engineering to tune the electrical properties of ferroics, potentially paving the way for advancing dislocation technology in functional ceramics.

We report an intrinsic strain engineering, akin to thin filmlike approaches, via irreversible high-temperature plastic deformation of a tetragonal ferroelectric single-crystal BaTiO3. Dislocations well-aligned along the [001] axis and associated strain fields in plane defined by the [110]/[1¯10] plane are introduced into the volume, thus nucleating only in-plane domain variants. By combining direct experimental observations and theoretical analyses, we reveal that domain instability and extrinsic degradation processes can both be mitigated during the aging and fatigue processes, and demonstrate that this requires careful strain tuning of the ratio of in-plane and out-of-plane domain variants. Our findings advance the understanding of structural defects that drive domain nucleation and instabilities in ferroic materials and are essential for mitigating device degradation.