Although methylammonium lead iodide (MAPI) perovskite solar cells have reached efficiencies above 20%, the material is environmentally unstable. Mixing MAPI with lower dimensional (LD) perovskites has been suggested to improve its stability in recent studies. However, the LD-mixed perovskites have lower device performance, likely as a result of limited charge-carrier mobility due to their decreased structural dimensionality. To understand this effect, we mixed large-A-site cation LD perovskites, tert-butylammonium lead iodide, with MAPI, and performed a device performance diagnostics. The results suggested although the charge-carrier lifetime was improved, the mobility decreased by a factor of 20. This contributed to a reduction in device efficiency by 2 orders of magnitude, indicating that mobility plays an important role in 3D/LD perovskite mixtures.@en

Methylammonium lead iodide (MAPI) is a prototypical photoabsorber in perovskite solar cells (PSCs), reaching efficiencies above 20%. However, its hygroscopic nature has prompted the quest for water-resistant alternatives. Recent studies have suggested that mixing MAPI with lower dimensional, bulky-A-site-cation perovskites helps mitigate this environmental instability. On the other hand, low dimensional perovskites suffer from poor device performance, which has been suggested to be due to limited out-of-plane charge carrier mobility resulting from structural dimensionality and large binding energy of the charge carriers. To understand the effects of dimensionality on performance, we systematically mixed MA-based 3D perovskites with larger A-site cations to produce dimethylammonium, iso-propylammonium, and t-butylammonium lead iodide perovskites. During the shift from MAPI to lower dimensional (LD) PSCs, the efficiency is significantly reduced by 2 orders of magnitude, with short-circuit current densities decreasing from above 20 mA cm-2 to less than 1 mA cm-2. In order to explain this decrease in performance, we studied the charge carrier mobilities of these materials using optical-pump/terahertz-probe, time-resolved microwave photoconductivity, and photoluminescence measurements. The results show that as we add more of the low dimensional perovskites, the mobility decreases, up to a factor of 20 when it reaches pure LD perovskites. In addition, the photoluminescence decay fitting is slightly slower for the mixed perovskites, suggesting some improvement in the recombination dynamics. These findings indicate that changes in structural dimensionality brought about by mixing A-site cations play an important role in determining the measured charge carrier mobility, and in the performance of perovskite solar cells.@en