A commonly used strategy in the fabrication of organic electronics involves the use of orthogonal solvents, i.e. the alternating use of organic solvents and water for the application of consecutive layers to prevent dissolution of previous layers. This strategy therefore requires the deposition of sequential layers with a large mismatch in surface energy. In case of organic photovoltaics (OPV) a particularly challenging deposition is that of the aqueous Poly(3,4-ethylenedioxythiophene) Polystyrene sulfonate (PEDOT:PSS) on the hydrophobic Poly(3-hexylthiophene-2,5-diyl/Phenyl-C61-butyric acid methyl ester (P3HT/PCBM) layer. The mismatch in surface energy causes dewetting and inhomogeneous layer formation. In inkjet printing individually placed droplets should spread sufficiently far to form a homogeneous closed layer before the solvents in the droplet evaporate. A formulation for the aqueous PEDOT:PSS layer has been developed in which the combination of solvents and surfactants is essential for achieving a homogenous layer on the timescales needed for inkjet printing. Homogenous layers of PEDOT:PSS on P3HT/PCBM were achieved for layer thicknesses from 400 nm to 50 nm. The efficiency of the OPV's fabricated with the new formulation were comparable with reference devices, where evaporated molybdenum oxide (MoO_x) was used as a topelectrode. This shows that by the addition of solvents and surfactants a hydrophilic solution can be inkjet printed successfully to form homogenous layers on hydrophobic surfaces and achieve good efficiencies in an inverted organic solar cell.

Inkjet printing (IJP) is a highly versatile and useful tool for product development, prototyping, and even small-scale manufacturing in the printed electronics industry. This chapter discusses a number of printed electronic (PE) applications. PE applications make use of inkjet-printed electrically conductive structures. At first sight, IJP might not seem the most obvious method for the manufacturing of these structures and as a result, it is rather new for PE manufacturing. The potential of IJP for PE applications has been demonstrated recently in a variety of academic and industrial research laboratories. These examples are, however, usually achieved on a sheet-to-sheet (S2 S) basis and only on a small scale. Various types of functional electronic materials can be processed into functional structures and devices by IJP. Examples include conductive metallic inks, organic semiconductors, insulators, and many others.