This research aimed to investigate the attenuation mode of the layer modulus of asphalt pavement in accelerated pavement testing (APT). A full-scale experimental section was constructed and tested using the APT facility. Two non-destructive testing (NDT) methods, named falling weight deflectometer (FWD) technique and portable seismic property analyzer (PSPA) test, were used to obtain the layer moduli of asphalt pavement during the APT test. The variation patterns of layer moduli obtained by FWD and PSPA tests were calculated and compared after the temperature was corrected to 20 ℃. It was found that the variation pattern of surface layer modulus based on field FWD measurements was consistent with the one measured from PSPA tests. That is the modulus of the surface layer increases with the APT load repetitions firstly and then decreases with the rise of the repetitions. The modulus values of the surface layer measured from PSPA tests are obviously larger than those backcalculated based on deflection basins. The ratio of the measured surface layer modulus based on the PSPA test to the backcalculated one based on the FWD test ranges between 2.06 and 2.71. The backcalculated base layer modulus always declines with the increasing loading repetitions. The attenuation patterns of the surface layer modulus and the base layer modulus in the damage stage are described as E_a=421100*N^-0.6119 and E_b=128000*N^-0.1096, respectively.

In a mechanistic-empirical (ME) pavement design method, the modulus of asphalt concrete (AC) is essential. The in-situ AC modulus can be obtained by the surface wave method (SWM). However, the measured modulus needs to be adjusted to the design frequency values. This study aimed to propose a frequency adjustment method for the in-situ AC seismic modulus. For this purpose, coring and dynamic modulus tests, FWD (Falling Weight Deflectometer) tests, and PSPA (Portable Seismic Pavement Analyzer) tests were carried out in the accelerated pavement test (APT). The master curves generated by the dynamic modulus results correlated well with the moduli determined from the other tests. Based on this relationship, a frequency adjustment factor was developed for the seismic modulus of the undamaged AC layer. For the damaged AC layer, the proposed factor was modified by incorporating the effect of the damage. Finally, to validate the frequency adjustment factor, the measured maximum tensile strains in the APT were compared with the values determined from the adjusted seismic moduli. The results prove that the frequency adjustment factor is appropriate to obtain the design modulus from the surface wave test. The PSPA test is also recommended to obtain the in-situ AC seismic modulus.