The study of buckling and post-buckling behavior of laminated composites consisting multiple delaminations using acoustic emission
Anvar Sobhani (Amirkabir University of Technology)
M. Saeedifar (Amirkabir University of Technology, TU Delft - Structural Integrity & Composites)
Mehdi Ahmadi Najafabadi (Amirkabir University of Technology)
Mohamad Fotouhi (University of the West of England)
D. Zarouchas (TU Delft - Structural Integrity & Composites)
More Info
expand_more
Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.
Abstract
This study introduces a comprehensive set of designed and tested glass/epoxy composites, AE monitoring and signal processing techniques; (i) to investigate the effect of multiple delaminations on buckling and post-buckling behaviors of laminated composites and (ii) to evaluate Acoustic Emission (AE) technique ability to monitor the buckling delamination growth and to classify the occurred damage mechanisms. The pre-delaminations were made by inserting a Teflon film at the plies interfaces during fabrication. Three different types of specimens were fabricated and subjected to compression loading to study the effects of the location, the number of delaminations, and the thickness of the Teflon film on buckling and post-buckling behaviors of the specimens. The mechanical results showed that the number of delaminations has a major effect on the critical and maximum loads and the location of delamination and the thickness of the Teflon film have minor effects on the critical and maximum loads. The AE signals of the specimens were then classified using Gaussian Mixture Model (GMM) and the evolution of different damage mechanisms was investigated. The AE results showed that AE is a robust technique to classify damage mechanisms in buckling of laminated composites and could identify delamination propagation earlier and with a lower standard deviation, compared with the conventional methods.