The impact of atmospheric species on the degradation of CIGS solar cells

Journal article (2015)

Authors

M.J. Theelen Photovoltaic Materials and Devices - EEMCS , TNO/Solliance
C Foster TNO/Solliance
H Steijvers TNO/Solliance
Nicolas Barreau Université de Nantes
Z. Vroon TNO/Solliance
M. Zeman Electrical Sustainable Energy
Research Group
Photovoltaic Materials and Devices (EEMCS) (TU Delft)
More Info
expand_more

Published Date

2015-10

Language

English

Reuse Rights

Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.

Faculty

Electrical Engineering, Mathematics and Computer Science

Department

Electrical Sustainable Energy

Research Group

Photovoltaic Materials and Devices

Abstract

CIGS solar cells were exposed to liquid water purged with the atmospheric gases carbon dioxide (CO2), oxygen (O2), nitrogen (N2) and air in order to investigate their chemical degradation behavior. The samples were analyzed by electrical, compositional and optical measurements before, during and after exposure in order to follow the degradation behavior of these solar cells in time. The solar cells showed a rapid decrease in conversion efficiency when exposed to water purged with a combination of CO2 and N2 as well as to water purged with air, while their efficiency was slowly reduced in unpurged water and water purged with N2 or O2. Cross-section SEM showed that the exposure of samples to H2O with large concentrations of CO2 led to the dissolution of the ZnO:Al layer, likely starting from the grain boundaries. This resulted in an increased series resistance, which is likely related to an increase in resistivity of the ZnO:Al layer. It also led to a very rapid decrease of the short-circuit current of these samples. Therefore, the conversion efficiency was rapidly lost.